Jewelry Resin

Castable Wax Jewelry Resin

Tensile Strength (MPa): 5.82 ±10%
Tensile Modulus (MPa): 46.73 ±10%
Elongation at Yield Point (%): 8.80 ±10%
Flexural Modulus (MPa): 161.15 ±10%
Flexural Strength (MPa): 4.34 ±10%
Notched Impact Strength (J/m): 37.50 ±10%
Maximum Force (KGF): 24.70 ±10%
Maximum Force of Deformation (mm): 7.30 ±10%
Elongation at Break (%): 13.06 ±10%
Hardness (Shore D): 50-60
Shrinkage Rate (%): 0.3-0.6
Viscosity (MPa.s): 80-150

Castable High Wax Jewelry Resin

Tensile Strength (MPa): 21.02 ±10%
Tensile Modulus (MPa): 209.35 ±10%
Elongation at Yield Point (%): 7.69 ±10%
Flexural Modulus (MPa): 425.80 ±10%
Flexural Strength (MPa): 16.50 ±10%
Notched Impact Strength (J/m): 86.70 ±10%
Maximum Force (KGF): 89.20 ±10%
Maximum Force of Deformation (mm): 12.02 ±10%
Elongation at Break (%): 21.25 ±10%
Hardness (Shore D): 60-70
Shrinkage Rate (%): 0.2-0.5
Viscosity (MPa.s): 150-230

Jewelry Mold Resin

Tensile Strength (MPa): 27.3 ±10%
Tensile Modulus (MPa): 316.6 ±10%
Elongation at Yield Point (%): 5.3 ±10%
Flexural Modulus (MPa): 773.8 ±10%
Flexural Strength (MPa): 37.2 ±10%
Notched Impact Strength (J/m): 76 ±10%
Maximum Force (KGF): 115.8 ±10%
Maximum Force of Deformation (mm): 9.0 ±10%
Elongation at Break (%): 16.1 ±10%
Hardness (Shore D): 80-88
Shrinkage Rate (%): 0.2-0.5
Viscosity (MPa.s): 150-300