Dental Resin

Ortho Model Resin

Tensile strength (MPa) 18.10 ± 10%
Tensile modulus ( MPa) 268.45 ± 10%
Elongation at yield point(%) 4.98 ± 10%
Flexural modulus (MPa) 397 . 96 ± 10%
Flexural strength (MPa) 21.72 ±10%
Notched impact strength (J/m) 74.30 ± 10%
Maximum force (KGF) 76 . 80 ± 10%
Maximum force of deformation 4.72 ± 10%
Elongation at break (%) 8.44 ± 10%
Hardness (Shore D) 88 - 80
Shrinkage rate(%) 0.2 - 0.5
Viscosity (MPa.S) 20 - 400

Temporary Restoration Resin

Hardness(Shore D) D85-90
Flexural modulus(MPa) 2000-3000MPa
Flexural strength(MPa) 100-140MPa
Tensile modulus(MPa) 1100-1500MPa
Tensile strength(MPa) 65-85MPa
Elogation at break(%) 10-15%
Water absorption(%） <1.0%
Cytotoxicity ISO 10993-5
Allergenicity ISO 10993-10

Surgical Guide Resin

Tensile strength (MPa) 26.78 ± 10%
Tensile modulus (MPa) 310.88 ± 10%
Elongation at yield point(%) 6.18 ± 10%
Flexural modulus (MPa) 761 . 26 ± 10%
Flexural strength (MPa) 25.19 ± 10%
Notched impact strength(J/m) 31.80 ± 10%
Maximum force (KGF) 113.60 ± 10%
Maximum force of deformation 13.87 + 10%
Elongation at break (%) 24 . 45 ±10%
Hardness (Shore D) 80-83
Viscosity (MPa.S) 120-180

Dental Casting Resin

Tensile strength (MPa) 30.59± 10%
Tensile modulus (MPa) 433.67 ± 10%
Elongation at yield point(%) 6.22 ± 10%
Flexural modulus (MPa) 811.08 ± 10%
Flexural strength (MPa) 39.81 ±10%
Notched impact strength (J/m) 113.97 ± 10%
Maximum force (KGF) 129.8 ± 10%
Maximum force of deformation 5.04 ± 10%
Elongation at break (%) 8.85 ± 10%
Hardness (Shore D) 85 - 88
Viscosity (MPa.S) 50 - 170

Try-in Dental

Tensile strength (MPa) 38.68 ± 10%
Tensile modulus (MPa) 447.12 ± 10%
Elongation at yield point(%) 7.22 ± 10%
Flexural modulus (MPa) 979.24 ± 10%
Flexural strength (MPa) 44.15 ±10%
Notched impact strength (J/m) 454.37 ± 10%
Maximum force (KGF) 162.76 ± 10%
Maximum force of deformation 6.80 ± 10%
Elongation at break (%) 35.44 ± 10%
Hardness (Shore D) 80 - 88
Viscosity (MPa.S) 350 - 650

Denture Base Resin

Tensile strength (MPa) 22.89± 10%
Tensile modulus (MPa) 232.05. ± 10%
Elongation at yield point(%) 6.92 ± 10%
Flexural modulus (MPa) 327.96 ± 10%
Flexural strength (MPa) 15.05 ±10%
Notched impact strength (J/m) 86.90 ± 10%
Maximum force (KGF) 105.10 ± 10%
Maximum force of deformation 8.45 ± 10%
Elongation at break (%) 14.91 ± 10%
Hardness (Shore D) 80 - 85
Viscosity (MPa.S) 200-450

Crown & Bridge Dental Resin

Tensile strength (MPa) 30.00 ± 10%
Tensile modulus (MPa) 490.91 ± 10%
Elongation at yield point(%) 6.36 ± 10%
Flexural modulus (MPa) 927.13 ± 10%
Flexural strength (MPa) 30.98 ±10%
Notched impact strength (J/m) 32 ± 10%
Maximum force (KGF) 127.3 ± 10%
Maximum force of deformation 3.65 ± 10%
Elongation at break (%) 6.45 ± 10%
Hardness (Shore D) 80 - 90
Viscosity (MPa.S) 150 - 250

Gingiva Mask Resin

Tensile strength (MPa) 1.33 ± 10%
Tensile modulus (MPa) 1.32 ± 10%
Elongation at yield point(%) 40.62 ± 10%
Maximum force (KGF) 5.64 ± 10%
Maximum force of deformation 60.7± 10%
Elongation at break (%) 110.28 ± 10%
Hardness (Shore A) 50-60
Viscosity (MPa.S) 350-550

Water-washable Ortho Model Resin

Tensile strength (MPa) 22.89 ± 10%
Tensile modulus (MPa) 232.05 ± 10%
Elongation at yield point(%) 6.92 ± 10%
Flexural modulus (MPa) 327.96 ± 10%
Flexural strength (MPa) 15.05 ±10%
Notched impact strength (J/m) 86.90 ± 10%
Maximum force (KGF) 105.10 ± 10%
Maximum force of deformation 8.45 ± 10%
Elongation at break (%) 14.91 ± 10%
Hardness (Shore D) 80 - 85
Viscosity (MPa.S) 200 - 450

Removable Die Dental Resin

Hardness(Shore D) 85-90
Flexural modulus(MPa) 1500-2000MPa
Elongation at break(%) 10-15%
Flexural strength(MPa) 60-80MPa
Cytotoxicity ISO 10993-5
Allergenicity ISO 10993-10
Irritate ISO 10993-10